CE MATERIAU EST OBTENU PAR UN TRAVAIL SOUS VIDE DE QUARTZ CONCASSE, MELANGE AVEC 7-8% ENVIRON DE RESINE POLYESTER. A CE MELANGE, IL EST AJOUTE DES COLORANTS ORGANIQUES, INORGANIQUES ET DES INGREDIENTS DE NATURE DIFFERENTES COMME ELEMENTS EN VERRE, LA NACRE…
POUR LA POSE, IL EST RECOMMANDE DE POSER CE MATERIAU EN MODE COLLE AVEC DES ADHESIFS BI-COMPOSANTS A BASE DE LATEX. LA POSE SCELLEE AVEC SABLE ET CIMENT EST EXCLUE POUR CE TYPE DE MATERIAU.
FINITION POLIE MAIS AUSSI EN FINITION JAIPUR (SURFACE IRREGULIERE AVEC EFFET ONDULE PLISSE) ET FINITION SATIN (FINITION SATINE BROSSE) - VOIR FICHES ET RESULTATS DE TEST CORRESPONDANTS.
FORMATS DISPONIBLES :
DALLES CALIBREES AVEC BORDS CHANFREINES FINITION POLIES DIMENSIONS 30x30, 30x60, 40x40, 60x60, 60x120 ET 120x120 CM, EPAISSEUR 1.3 CM. EXISTE EGALEMENT EN TRANCHES AVEC BORDS NON FINIS DIMENSIONS 125x125 ET 140x305 CM, EPAISSEUR 2 OU 3 CM ET EN PLINTHE DIMENSIONS 60x8x1.3 CM AVEC UN BORD CHANFREINE OU ARRONDI.
RESULTATS DES TESTS :
MASSE VOLUMIQUE APPARENTE 2413 kg/m³ (EN 14617-1 :2005)
COEFFIENT D’ABSORPTION 0.0 % (EN 14617-1 :2005)
MODULE DE RUPTURE 51.0 MPa (EN 14617-2 :2005)
TEST DE GLISSEMENT SEC 42 SRV (prEN 14617-3 :2003)
MOUILLE 7 SRV
RESISTANCE A L’ABRASION PROFONDE 12.8 MM (EN 14617-4 :2005)
RESISTANCE AUX CHOCS 5 JOULE (EN14617-9 :2005)
RESISTANCE CHIMIQUE CLASSE C4 (EN 14617-10 :2005)
MICRODURETE KNOOP 5583 MPa (EN 14617-14 :2003)
RESISTANCE A LA COMPRESSION 203 MPa (EN 14617-15 :2005)
RESISTANCE AU FEU CLASSE 1 (UNI 8457 / 1987 et 9174 / 1987).